| Brand Name: | INNOVACERA |
|---|---|
| Model Number: | INCA001 |
| Material: | Alumina Ceramic |
| Application: | Industrial Ceramic |
| Type: | Ceramic Plates |
| Place of Origin: | China (Mainland) |
| Density:: | 3.65-3.90g/cm3 |
| Open Porosity: | 0% |
| Color: | White ,Yellow |
| Bending Strength: | >300Mpa |
| Vickers Hardness HV 5: | >1500N/mm2 |
| Fracture Toughness: | >3.8MPa*m1/2 |
| Weibull Modulus: | 12 |
| Thermal Conductivity: | 30W/(m*K) |
Quick Details
Specifications
Alumina Ceramic Tile for Wear Resistance/Bulletproof/Innovacera
Company Information
We are a leading and biggest researcher and manufacturer of alumina ceramics in China,our products are very popular with customers from many countries all over the world,we will always offer your ceramics with high quality,high density,high hardness,accurate size and also we could delviery very fast.
Properties
low density
high hardness
high mechanical strength
dimensional stability (specific stiffness)
resistance to wear
resistance to corrosion (resistance to chemical attack)
weathering resistance
high working temperature
low or high thermal conductivity
good electrical insulation
dielectric and ferroelectric properties
Wear Parts
Ceramic Nozzles
Ceramic Sprayers Cyclones
Homogenising devices
Ceramic Linings
Milling Systems
Ceramic Thread guides
Applications
Wire and thread guides
Mechanical seals
Seal faces
Valve seats
Machine components
High temperature electrical insulators
High voltage insulators
Electronic components & substrates
Ballistic Armor
Roller & Ball Bearings
Wear resistant linings
Semiconductor parts
Laser cavities
Tap plates
Shot blast nozzles
Knife Sharpeners
Precision shafts and axles in high wear environments
Technical Data of Alumina Cermaic(Material Alumina 99%)
| Density | g/cm3 | 3.90±0.02 |
| Open Porosity | % | 0 |
| Average Crystalite Size | um | 5--10 |
| Color | Yellow | |
| Bending Strength | Mpa | >300 |
| Vickers Hardness HV5 | N/mm2 | >1500 |
| Fracture Toughness | Mpa*m1/2 | >3.8 |
| Weibull Modulus | 12 | |
| Thermal Expansion(0--1000degree C) | 10-6 | 8.5 |
| Thermal Conductivity | W(m*k) | 30 |
| Max. Working Temperature | °C | 1700 |