| Brand Name: | LONGTAI |
|---|---|
| Model Number: | LT-GL-50 |
| Refractoriness (Degree): | Common (1580°< Refractoriness< 1770°) |
| Al2O3 Content (%): | 50% |
| Material: | Mullite |
| Shape: | Powder |
| Place of Origin: | China (Mainland) |
| Package: | 50kg/bag |
| Al2O3: | 38-55% |
Quick Details
Specifications
Light Weight Aggregate Features:
Lightweight refractory aggregate is the main raw material for formulating lightweight refractory concrete.
We can choose different kinds of lightweight refractory aggregate according to different using temperature
of the lightweight concrete.
Light Weight Aggregate Applications:
1.Used as refractory linings that applied in roller kiln, tunnel kiln, intermittent shuttle kiln, furnace, etc.
2.As well as direct contact with the flame of the furnace insulating layer,instead of fire bricks.
3.The products widely used in metallurgy, petrochemical, machinery, electrical industry
Light Weight Aggregate Physiochemical Index:
|
Item |
Properties |
|||||||
|
Mullite Refractory Aggregates |
High Alumina Refractory Aggregates |
Clay Refractory Aggregates |
lytag |
|||||
|
Brand |
YQM
|
YQL-1
|
YQL-2
|
YQN-1
|
YQN-2
|
YQT
|
||
|
Packing density g/cm3 |
0.7-1
|
0.65-0.85
|
0.6-0.8
|
0.65-0.8
|
0.6-0.9
|
0.6-0.75
|
||
|
Compression strength MPa |
3
|
2.5
|
2
|
2.5 |
2
|
1.5
|
||
|
% Reheat linear change |
1400X3
|
1350X3
|
1350X3
|
1300X3
|
1300X3
|
1300X3
|
||
|
Al2O3
|
60 |
50 |
48
|
38
|
65
|
20 |
||
|
Fe2O3 |
1
|
1.2 |
2
|
1.3
|
2.5
|
3.5 |
||
|
Refractoriness,°C |
1770
|
1730 |
1710 |
1690 |
1650 |
1580 |
||
|
Application |
All industrial furnace |
|||||||