Technical Data
|
|
Property
|
Test method
|
Values
|
|
Physical
|
Tensile strength
|
When test at 500mm/min.
|
≥12 MPa
|
|
|
Breakdown elongation
|
When test at 500mm/min.
|
≥300%
|
|
Aging (158℃ /168hrs)
|
Tensile strength
|
When test at 500mm/min.
|
≥10MPa
|
|
Breakdown elongation
|
When test at 500mm/min.
|
≥200%
|
|
|
Density
|
--
|
1.15~1.25
|
|
|
Thermal endurance
|
--
|
125 ℃
|
|
|
Hardness (Shore D)
|
--
|
≤ 40 HD
|
|
|
Water absorption (23℃/24hrs)
|
--
|
≤0.5%
|
|
|
Low temperature flexibility(-30℃/1hr)
|
--
|
No cracking
|
|
|
Peel strength to steel
|
ASTM D2671
|
80N/25mm
|
|
|
Peel strength to XLPE
|
ASTM D2671
|
110N/25mm
|
|
|
Heat shock (250℃/4hrs)
|
--
|
No cracking,No drop, No flow(outer layer only)
|
|
Electrical
|
Volume resistivity
|
ASTM D2671
|
≥1014 Ω.cm
|
|
|
Dielectric strength(2500V AC/60s)
|
ASTM D2671
|
≥ 12KV/mm
|
|
|
Dielectric breakdown voltage
|
--
|
≥ AC 2500V
|
|
|
Dielectric voltage Withstand
|
1min.AC2500V
|
No breakdown
|
|
Aging(158 ℃/168hrs)
|
Dielectric breakdown voltage
|
--
|
AC 2500V min. and more than 50% of the value
obtained with unaged sample
|
|
Dielectric voltage withstand
|
1min.AC2500V
|
No breakdown
|
|
Chemical
|
Flammability(outer layer only)
|
VW-1
|
Pass
|
|
|
Copper corrosion
|
(158℃/168hrs) 500mm/min
|
Elongation≥100%
|
|
Fluid resistance 23℃/24hrs
|
Diesel fuel(bs2869 class A1)
|
ISO 37
|
Tensile strength
|
≥7 MPa
|
|
Hydraulic fluid(H-515)
|
Breakdown elongation
|
≥300%
|
|
Lubricating oil(O-149)
|
Peel strength to steel
|
60N/25mm
|
Note: The test methods conform to UL224.
|
Dimensions
|
3:1
|
|
Reference
|
As supplied(mm)
|
After recovered(mm)
|
Standard length
|
|
UPM S3(t)
|
ID min.
|
ID max.
|
WT nom.
|
m
|
|
Shrink Ratio: 3:1
|
|
|
|
|
|
3.2/1.0
|
3.2
|
1.0
|
1.0
|
200
|
|
4.8/1.6
|
4.8
|
1.6
|
1.0
|
100
|
|
6.4/2.1
|
6.4
|
2.1
|
1.0
|
100
|
|
7.9/2.6
|
7.9
|
2.6
|
1.4
|
50
|
|
9.5/3.2
|
9.5
|
3.2
|
1.4
|
50
|
|
12.7/4.2
|
12.7
|
4.2
|
1.7
|
1.22
|
|
15.0/5.0
|
15.0
|
5.0
|
1.8
|
1.22
|
|
19.1/6.0
|
19.1
|
6.0
|
2.2
|
1.22
|
|
25.4/8.0
|
25.4
|
8.0
|
2.5
|
1.22
|
|
30.0/10.0
|
30.0
|
10.0
|
2.5
|
1.22
|
|
39.0/13.0
|
39.0
|
13.0
|
2.5
|
1.22
|
|
51.0/17.0
|
51.0
|
17.0
|
2.6
|
1.22
|
|
Shrink Ratio: 4:1
|
|
4.0/1.0
|
4.0
|
1.0
|
1.0
|
1.22
|
|
6.0/1.5
|
6.0
|
1.5
|
1.0
|
1.22
|
|
8.0/2.0
|
8.0
|
2.0
|
1.0
|
1.22
|
|
12.0/3.0
|
12.0
|
3.0
|
1.4
|
1.22
|
|
16.0/4.0
|
16.0
|
4.0
|
1.7
|
1.22
|
|
20.0/5.0
|
20.0
|
5.0
|
1.8
|
1.22
|
|
24.0/6.0
|
24.0
|
6.0
|
2.2
|
1.22
|
|
32.0/8.0
|
32.0
|
8.0
|
2.5
|
1.22
|
|
52.0/13.0
|
52.0
|
13.0
|
2.5
|
1.22
|
|
|
|
|
|
|
|
ID=Internal Diameter
|
WT=total wall thickness
|
|
|
|
Typical application
|
|
Ideal for applications including connector-to-cable sealing, wire harness bundles and splices
|
|
where insulation, corrosion resistance and mechanical stress relief are required.
|
|
Ordering
|
|
Standard color : Black
|
|
Special colors(eg.White,Red,Yellow,Green,Clear) are available on request
|
|
Standard packaging on spools and/or 1.22m/pc
|
|
Please specify specification, color, quantity when ordering
|
|
Cross reference
|
|
Raychem/ Tyco :ATUM
|
|