| Brand Name: | SUNTHERM |
|---|---|
| Model Number: | High Zirconium |
| Place of Origin: | China (Mainland) |
| Thermal Conductivity: | 0.085-0.18w/(m.k) |
| Fiber Diameter: | 3-5um |
| Working Temperature: | 1350C |
| Ultimate Strength (≥ MPa): | 0.5 |
| Chemical Composition: | AL2O3:39-40%;ZrO2:15-17% |
| Grade: | HZ (High Zirconium) |
| Length: | 900/600/1200/2500mm |
| Width: | 300/600/1000/1200mm |
| Thickness: | 3-80mm |
| Density: | 280-600kg/m3 |
| Color: | Pure White |
| MSDS Available: | Yes |
| Samples: | Available |
Quick Details
Specifications
SUNTHERM Aluminum silicate ceramic fiber board takes ceramic fibers as the main
raw materials ,After fiber processing, slag removing, then add some organic and inorganic
binder, through vacuum forming process, to be made into high strength fiber board.
Product information
|
Item |
Ceramic fiber board |
|
Type |
Standard,High Pure, High Aluminum ,Al-Zirconium,Zirconium. |
|
Classification Temperature |
1260°C,1360°C,1430°C |
|
Applications |
? Applications that require high-temper, high strength from the load-bearing areas. ? For high air flow, mechanical damaging large areas of industrial furnace wall lining, door and roof seals ? Construction, fire doors, fire wall fire insulation ? High-temperature pipe wall lining ? High-temperature furnace insulation ? High temperature gasket ? Glass tank furnace insulation panels ? Furnace roof insulation ? Molten metal delivery system ? Combustion chamber insulation ? Ladle furnace backing ? Shipping, aviation, precision industrial equipment ? Heating equipment, household appliances,other high-end applications |
|
Features |
? Rigid, free support
? Easy to shape or cutting
? Acoustic performance
? Non-brittle material, good elasticity
? Size can be accurate to ± 1mm
? Low heat capacity, low thermal conductivity
? Resistance to wind and erosion,long service life ? High strength and excellent machinability. |
|