Length: | 3000-18000mm |
---|---|
Width: | 1500-4300mm |
Special Use: | Wear Resistant Steel |
Application: | Container Plate |
Surface Treatment: | Coated |
Type: | Steel Plate |
Model Number: | CORTEN STEEL |
Brand Name: | SYISTEEL |
Place of Origin: | China (Mainland) |
Thickness: | 3-150MM |
Grade: | CORTEN A-B |
Standard: | AISI,ASTM,BS,DIN,GB,JIS |
PACKAGE: | STANDARD |
Quick Details
Specifications
CORTEN Steel Grade-A / CORTEN Steel Grade-B / S355JOWP / S355JOWP+N / S355J2WP
Chemical Composition (heat analysis, %)
In order to obtain fine grain structure a sufficient amount of nitrogen absorbing elements is added (e.g. ≥0.02% Al).
EQUIVALENT SPECIFICATIONS
/ S355J2WP+N / S355JOW / S355JOW+N / S355J2W / S355J2W+N
SPA-H ATMOSPHERIC CORROSION RESISTANT STEEL / WEATHER RESISTANT STEEL SHEET;
Scope
COR-TEN A applies to plates up to 60mm in thickness, COR-TEN B applies to plates up to 100 mm in
thickness.
Definition
Weathering means that due to their chemical compositions COR-TEN A and COR-TEN B steels, when utilized
unprotected, exhibits increased resistance to atmospheric corrosion compared to unalloyed steels. This is
because it forms a protective layer on its surface under the influence of the weather.
Applications
The steel is used for various types of welded, bolted and riveted constructions e.g. steel frame structures,
bridges, tanks and containers, exhaust systems, vehicles and equipment constructions.
Basic guidelines for the use of this steel in the unprotected condition are described in EN 10025-5 and
DASt rule 007.
Grade
C
Si
Mn
P
S
Cr
Cu
V
Ni
COR-TEN A
0.12
0.25-0.75
0.20-0.50
0.07-0.15
0.030
0.50-1.25
0.25-0.55
-
0.65
COR-TEN B
0.16
0.30-0.50
0.80-1.25
0.030
0.030
0.40-0.65
0.25-0.40
0.02-0.10
0.40
Mechanical Properties, in the state of delivery condition
At room temperature for plates ≥3mm in thickness (transverse test specimans, according to EN 10002). Requirements to hot rolled plates ≤3mm in thickness according to EN 10025-5.
Grade
Minimum yield point (ReH Mpa *)
Tensile strength Rm MPa
Minimum elongation A (Lo=5.65 √So) %
COR-TEN A
355
470-630
20
*) 1 Mpa = 1N/mm2
In case of cold rolled material the yield point is min. 310 Mpa and the tensile strength min. 445 MPa. Furthermore cold rolled sheets ≤3mm in thickness made of steel grade COR-TEN A-F for increased demand to the cold formability is available.
Mechanical properties:
Grade
Material thickness mm
Minimum yield point (ReH Mpa *)
Tensile strength Rm MPa
Minimum elongation A (Lo=5.65 √So) %
COR-TEN B
≤16
355
470-630
20
≤16
345
*) 1 Mpa = 1N/mm2
The notched-bar impact energy is determined on ISO-V longitudinal test specimens at a temperature of - 20°C as an average of three tests. For product thicknesses ≥10mm the average value is at least 27 J. For thicknesses between 10mm and 6mm, the minimum impact value is reduced proportionally to the specimen width (product thickness).
No impact test is performed on products below 6mm in thickness.
Number of Tests
*) as referenced in EN 10025-5
Material #
EN 10155
SEW 087
NFA 35-502
UNI
BS 4360
UNE
ASTM
JIS G3114
1.8961
S235J2W
WTSt 37-3
E 24 W 4
Fe 360 DK 1
-
-
-
-
1.8945
S355J0WP
E 36 WA 3
Fe 510 C1K1
WR 50 A
-
-
-
-
1.8946
S355J2WP
-
E 36 WA 4
Fe 510 D1K1
-
-
A 242 Type 1
-
1.8959
S355J0W
-
E 36 WB 3
Fe 510 C2K1
WR 50 B
-
A 588 - A 242 Gr. 1
SMA 50 AW
1.8963
S355J2G1W
WTSt 52-3
-
Fe 510 D2K1
WR 50 C
-
A 588 Gr. A
to
1.8965
S355J2G2W
-
-
-
-
-
-
SMA 50 CP
1.8966
S355K2G1W
-
E 36 WB 4
-
-
-
A 709 Gr. 50 W
-
1.8967
S355K2G2W
-
-
-
-
-
-
-