Details of HJ431:
HJ431 is a kind ofsmelting-type,red brown to light yellow colored,glassy granulated flux with high manganese and silicon but low fluorine,mesh 8-14(2.5-1.5mm),8-40(2.5-0.45mm) and 14-40(1.5-0.45mm). Either alternating or direct current can be used and Welding wires must be connected with the positive electrode when direct current is used. The welding technology has good performance.
APPLICATIONS:
In combination with H08A, H08MnA AND H10Mn2 wires, this flux is suitable for welding of low carbon steels and some low alloy steel such as 16Mn and 15Mnv in producing of structures, boilers, ships, pressure vessels, ect. It can also be used for electroslag welding.
Cautions:
1.The oil soil,moisture,iron rust and other foreign substances must be removed from the surface before welding.
2.The flux must be baked under 300-400oC for 2 hours.
TYPICAL FLUX COMPOSITION RANGE:(%)
Mechanical Performance:
Our Factory Introduction :
LAIWU HULING WELDING is one of leading biggest manufacturer of Submerged ARC welding flux in China. The annual capacity of production is growing and up to12000 metric tons of agglomerated flux and 5000 metric tons of fused flux. The factory has established the R&D laboratory with the advanced inspection equipments in field of welding materials. Our company is located at Laiwu City near by the Jinan International Airport, and also is near the TAISHAN Mount of Shandong Province, China.
The Submerged-ARC welding flux has been approved and passed the inspection of quality with the province grade and the national grade in China. We strictly executed and produced the welding flux according to the industrial standards of GB/T 5293-1999, GB/T 12740-2003, GB/T17854-1999 and the China Classification Society-1996 completely. Our quality management has passed IS09001-2008 Quality System Certification.
The welding flux has been widely used in the Chemical engineering equipment, Heavy machinery, Pressure vessel, Boiler, Gas cylinder body, Spiral welded steel pipe, Steel structure building H-beam steel etc. We have been exported the welding flux to India, Indonesia, Egypt, Japan, Philippine and Jordan. The foreign customer usually purchased and preferred to the high quality Agglomerated flux ( LH-SJ101;LH-SJ301;LH-SJ501;LH-HF101G ) and Manganese oxide fused flux.
HJ431 is a kind ofsmelting-type,red brown to light yellow colored,glassy granulated flux with high manganese and silicon but low fluorine,mesh 8-14(2.5-1.5mm),8-40(2.5-0.45mm) and 14-40(1.5-0.45mm). Either alternating or direct current can be used and Welding wires must be connected with the positive electrode when direct current is used. The welding technology has good performance.
APPLICATIONS:
In combination with H08A, H08MnA AND H10Mn2 wires, this flux is suitable for welding of low carbon steels and some low alloy steel such as 16Mn and 15Mnv in producing of structures, boilers, ships, pressure vessels, ect. It can also be used for electroslag welding.
Cautions:
1.The oil soil,moisture,iron rust and other foreign substances must be removed from the surface before welding.
2.The flux must be baked under 300-400oC for 2 hours.
TYPICAL FLUX COMPOSITION RANGE:(%)
| SiO2+MnO | CaF2+CaO | Al2O3+MgO | S | P |
| 74-80 | 10-14 | 9-12 | ≤0.06 | ≤0.08 |
Mechanical Performance:
| Tested Items |
s (Mpa) |
b (MPa) |
δ5 |
AKV(-20oC) (J) |
| Common Results | ≥340 | ≥420~550 | ≥22% | ≥34 |
Our Factory Introduction :
LAIWU HULING WELDING is one of leading biggest manufacturer of Submerged ARC welding flux in China. The annual capacity of production is growing and up to12000 metric tons of agglomerated flux and 5000 metric tons of fused flux. The factory has established the R&D laboratory with the advanced inspection equipments in field of welding materials. Our company is located at Laiwu City near by the Jinan International Airport, and also is near the TAISHAN Mount of Shandong Province, China.
The Submerged-ARC welding flux has been approved and passed the inspection of quality with the province grade and the national grade in China. We strictly executed and produced the welding flux according to the industrial standards of GB/T 5293-1999, GB/T 12740-2003, GB/T17854-1999 and the China Classification Society-1996 completely. Our quality management has passed IS09001-2008 Quality System Certification.
The welding flux has been widely used in the Chemical engineering equipment, Heavy machinery, Pressure vessel, Boiler, Gas cylinder body, Spiral welded steel pipe, Steel structure building H-beam steel etc. We have been exported the welding flux to India, Indonesia, Egypt, Japan, Philippine and Jordan. The foreign customer usually purchased and preferred to the high quality Agglomerated flux ( LH-SJ101;LH-SJ301;LH-SJ501;LH-HF101G ) and Manganese oxide fused flux.