Shape: | flat bar |
---|---|
Grade: | 1.2379 |
Standard: | DIN |
Quick Details
Specifications
1.2379/D2 is a high carbon, high chromium, molybdenum, vanadium, air hardening tool steel which offershigh surface hardness, good wear resistance, through hardening properties, dimensional stability and high resistance to tempering effect. 1.2379/D2 tool steel is also suitable for vacuum hardening.
C Si Mn P/S Cr Mo V
1.45-1.60 0.10-0.60 0.20-0.60 <=0.030 11.00-13.00 0.60-1.00 0.90-1.00
Forging:
Heat slowly and uniformly to 700°C then more rapidly to 900/1040°C. After forging 1.2379 cool slowly.
Annealing:
Anneal at 850°C and slow furnace cool. Hardness after annealing will be approx. 225 brinell.
Hardening:
Pre heat the 1.2379/D2 component slowly to 750/780°C and thoroughly soak. Continue heating to the final hardening temperature of 1000/1030°C and allow the component to be heated through. Quench in oil or cool in air.
C Si Mn P/S Cr Mo V
1.45-1.60 0.10-0.60 0.20-0.60 <=0.030 11.00-13.00 0.60-1.00 0.90-1.00
Forging:
Heat slowly and uniformly to 700°C then more rapidly to 900/1040°C. After forging 1.2379 cool slowly.
Annealing:
Anneal at 850°C and slow furnace cool. Hardness after annealing will be approx. 225 brinell.
Hardening:
Pre heat the 1.2379/D2 component slowly to 750/780°C and thoroughly soak. Continue heating to the final hardening temperature of 1000/1030°C and allow the component to be heated through. Quench in oil or cool in air.