Physical Performance

Typical Value

Test Method

Density, 23°C

1.46 g/cm³

ISO 1183-1 (ASTM D792)

Melt flow velocity (150°C/21.6kg)

7g/10min

ISO 1133, (b)

Mechanical Performance

Typical Value

Test Method

Tensile strength 250mm/min

12.0 MPa

IEC 60811-1-1

Elongation at break 250mm/min

200 %

IEC 60811-1-1

After aging 7d @ 110°C

IEC 60811-1-2

- Tensile strength 250mm/min

12.3 MPa

- Elongation at break 250mm/min

180 %

After aging 7d @ 100°C

IEC 60811-1-2

- Tensile strength 250mm/min

12.2 MPa

- Elongation at break 250mm/min

185%

Tearing strength

8 N/mm

BS 6469:99-1

High temperature pressure test 4h @ 90℃

35 %

IEC 60811-3-1

Environmental stress crack resistance (96hrs)

No cracking

IEC 60811-1-4/B

Low-temperature impact test @ -25℃

Ok

IEC 60811-1-4

Combustion Performance

Typical Value

Test Method

Oxygen index value¹

34 %

ISO 4589-2(ASTM D2863)

Smoke density

ASTM E-662

-  Flame (1mm) Ds max

50

-Flameless (1mm) Ds max

150

Toxicity index

1

NES 713

Combustion Performance

Typical Value

Test Method

Halogen content

0

IEC 60754-1

Halogen acid released

IEC 60754-2

-PH (min)

5.6

-Electrical conductivity (max)

0.5μS/mm

Vertical flame test

Ok²

IEC 60332-3

Smoke index

Ok²

IEC 61034

Electrical Performance

Typical Value

Test Method

Electric inductivity 50Hz (23°C-50%HR)

3.5

IEC 60250 (ASTM D150)

Dielectical strength

30MV/m

IEC 60243

Volume resistivity (23°C-50%HR)

2*10¹⁴Ω cm

IEC 60093 (ASTM D257)

Others

Typical Value

Test Method

Soaking test  168Hrs @ 70°C,

Volume resistivity (23°C-50%HR)

10¹³Ω cm

IEC 60093 (ASTM D257)

Thermal impack 1h @ 150°C

Ok³

IEC 60811-3-1

Shore-A

95

ISO R868 (ASTM D2240)

Thermal shrinkage percent 1h @ 100°C

1.5 %

IEC 60811-1-3