| Flux Content: | 0 |
|---|---|
| Application: | Bicycles,aluminum sccoter,engine carriage,pressure vessel,etc. |
| Weight: | 0.5kgs,2kgs,6kgs,7kgs |
| Melting Point: | 1060 - 1175 |
| Diameter: | 0.8mm,0.9m,1.0mm,1.2mm,1.6mm |
| Material: | Aluminum / Aluminum Alloy |
| Model Number: | 5356 |
| Brand Name: | SHUANGMA |
| Place of Origin: | China (Mainland) |
Quick Details
Specifications
Description:
MIG Welding wire ER5356 is widely used in general welding material with the magnesium of 5% and a little of Titanium fine grains. And this product is of high toughness, good forgeability, and well anti-corrosiveness, Furthermore, this is a good choice for color-match in welding after anodic process.
The model ER5356 do not suggested to use in aluminum alloy workpiece which working temperature is over 65℃,thus will cause corrosion cracking in welded joints. You should strictly clean the oxide film on the edge of the workpiece and oil before welding, otherwise it will make bad weld produce and cause porosity, slag inclusion and other defects. Also you can use a plate to hold molten metal to ensure meld form.
Usage:
The argon arc welding of Aluminum & Magnesium alloy welding wires is used as the filler material, widely used in welding among Al-Mg-Si, Almasilalloy and Aluminium & Magnesium alloy, like: bicycles, aluminum scoter, etc. engine carriage, pressure vessel, armory processing, ship-building. space shuttle etc.
|
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Zn |
Ti |
Be |
|
Al |
||||
|
≤0.25 |
≤0.4 |
≤0.1 |
0.05~0.2 |
4.5~5.5 |
0.05~0.20 |
≤0.1 |
0.06~0.20 |
≤0.0003 |
Rem. |
|
Melting range |
1060 - 1175°F |
|
Electrical conductivity |
29%IACS(O);27%IACS(H18) |
|
Density |
2.66g/mm3 |
|
Anti corrosion performance |
A(Gen) A(SCC) |
|
The coefficient of thermal expansion (20 ℃ ~300 ℃) |
23.7×10-6/K |
|
Thermal conductivity (20 ℃) |
110-150W/m·K |
Our Services
OEM is accepable
Purchase other welding consumables for clients for free
Company Information
Our comany is the biggest aluminum welding wire manufacturer in China,with 13,000 square meter factory and more than 200,000,000RMB fixed assets,is a collection of scientific research,development,manufacture,sales and service enterprise.Our company was found in 1998,located in the YunCheng city,which is one of the biggest Aluminum industry products park in China.From 2008 we started to export the aluminum and aluminum alloy welding wire to Russia,Ukraine,Korea,India and Thail etc.earning good reputation from our clients in the world.
|
The mechanical properties of the welding joints |
|
Motherboard |
Motherboard performance |
Joint properties |
|||||
|
Rm (MPa) |
RP0.2 (MPa) |
A/% |
Rm (MPa) |
RP0.2 (MPa) |
A/% |
||
|
6061-T6/T651 |
310 |
275 |
12 |
205 |
130 |
11 |
|
|
6063-T6 |
240 |
210 |
12 |
135 |
80 |
12 |
|
|
7005-T6/T63 |
370 |
315 |
12 |
315 |
205 |
10 |
|
|
7039-T64 |
445 |
380 |
13 |
300 |
170 |
13 |
|
|
5086-H32 |
290 |
205 |
12 |
265 |
115 |
17 |
|
|
5083-O |
310 |
200 |
16 |
285 |
120 |
15 |
|
|
6082-T6 |
310 |
275 |
11 |
210 |
130 |
10 |
|
Classification
GB10858-2008
ANSI/AWS A5.10-92
Passed ISO9001:2008 Quality Management System
Packaging & Shipping
|
Diameter /mm |
Packing /Kg |
|
|
MIG |
0.8,0.9,1.0,1.2,1.6,2.4 |
0.5,2,5,6,7 |
|
TIG |
1.6,2.0,2.4,3.0,3.2,4.0,5.0/1000 |
5,10 |
Why Choose us
1.Nearly 17 years of manufacturing history
2.Almost 10 years of exporting experience
3.The biggest Aluminum welding wire supplier for China Aluminum production industry
4.Fast delivery time guaranteed
5.Competitive price offering
6.Highest quality proved by big clients
7.Best service to every clients