| Flux Content: | 0 |
|---|---|
| Application: | Pressure vessle of chemical industry,nuclear industry,ship-building |
| Weight: | 0.5kgs,2kgs,6kgs,7kgs |
| Melting Point: | 1075 - 1180 |
| Diameter: | 0.8mm,0.9m,1.0mm,1.2mm,1.6mm,2.0mm,2.4mm,3.0mm,3.2mm,4.0mm,5.0mm,6.0mm |
| Material: | Aluminum / Aluminum Alloy |
| Model Number: | 5183 |
| Brand Name: | SHUANGMA |
| Place of Origin: | China (Mainland) |
Quick Details
Specifications
Description:
TIG Welding wire ER5183 is with nearly 5% magnesium and some of manganese. And this product is of high toughness, good forge-ability, and well anti-corrosive, Furthermore, this is a good choice for color-match in welding after anodize process.But for some alloy, the strength of welding joint is a little higher than 5356.
The model 5183 do not suggested to use in aluminum alloy pieceworker which working temperature is over 65℃,thus will cause corrosion cracking in welded joints. You should strictly clean the oxide film on the edge of the pieceworker and oil before welding, otherwise it will make bad weld produce and cause porosity, slag inclusion and other defects. Also you can use a plate to hold molten metal to ensure meld form.
The strength of ER5183 is higher than ER5356, which used in high strength situation, especially for crack after welding with other brand or other type aluminum welding wires. SAL5183 is with nearly 5% magnesium and some of manganese. And this product is of high toughness, good forgeability, and well anti-corrosiveness, Furthermore, this is a good choice for color-match in welding after anodic process.
Usage: The argon arc welding of Aluminum & Magnesium alloy welding wires is used as the filler material, used in pressure vessel of chemical industry, nuclear industry, ship-building, boiler, space industry, etc.
Chemical component
Chemical component(wt)/% |
|
Melting range |
1075 - 1180°F |
|
Electrical conductivity |
16~19Ω·m/mm2 |
|
Density |
2.66g/mm3 |
|
Anti corrosion performance |
A(Gen) A(SCC) |
|
The coefficient of thermal expansion (20 ℃ ~300 ℃) |
23.7×10-6/K |
|
Thermal conductivity (20 ℃) |
110-120W/m·K |
|
|
|
The mechanical properties of the welding joints |
|
Motherboard |
Motherboard performance |
Joint properties |
|||||
|
Rm (MPa) |
RP0.2 (MPa) |
A/% |
Rm (MPa) |
RP0.2 (MPa) |
A/% |
||
|
6061-T6/T651 |
310 |
275 |
12 |
205 |
130 |
11 |
|
|
6063-T6 |
240 |
210 |
12 |
135 |
80 |
12 |
|
|
7005-T6/T63 |
370 |
315 |
12 |
315 |
205 |
10 |
|
|
7039-T64 |
445 |
380 |
13 |
310 |
180 |
12 |
|
|
5083-O |
310 |
200 |
18 |
285 |
125 |
16 |
|
|
6082-T6 |
310 |
275 |
11 |
210 |
130 |
10 |
|
|
7039-T61 |
410 |
340 |
14 |
320 |
220 |
14 |
|
Classification
GB10858-2008
ANSI/AWS A5.10-92
Passed ISO9001:2008 Quality Management System
Packaging & Shipping
|
Diameter /mm |
Packing /Kg |
|
|
MIG |
0.8,0.9,1.0,1.2,1.6,2.4 |
0.5,2,5,6,7 |
|
TIG |
1.6,2.0,2.4,3.0,3.2,4.0,5.0/1000 |
5,10 |