Model Number: | 5052 |
---|---|
Brand Name: | Suzhou Southeast |
Place of Origin: | China (Mainland) |
Alloy Or Not: | Is Alloy |
Width: | 30-2000mm |
Thickness: | 0.3-30mm |
Application: | boat building,construction |
Type: | Plate |
Grade: | 5000 Series |
color: | silver |
surface: | mill finish |
standard: | GB/T3880-2006 |
price terms: | FOB,CIF,CFR |
Quick Details
Specifications
Chemical Composition
Cu |
0.10 |
Si+Fe |
0.45 |
Mn |
0.10 |
Mg |
2.2/2.8 |
Zn |
0.10 |
Cr |
0.15/0.35 |
Al |
Balance |
Characteristics
This is a non-heat treatable alloy that is weldable. It is hardened by cold work. It has good forming characteristics and good corrosion resistance, including resistance to salt water.
(1) Machinability
This alloy has relatively fair machinability. It is easier to machine in the
hard temper than as annealed and the quality of finish is better if machined in
the hard condition. Oil lubricants should be used for machining, except that
very light cuts may
(2) Forming
AL5052 is
readily formed at room temperature. Successive cold working decreases the
formability.
(3) Corrosion Resistance
Corrosion resistance to salt water and general atmospheric conditions is good.
(4) Welding
This alloy is readily welded by conventional methods. When filler rod is required
it should be aluminum alloy 5356 as filler. Either tungsten or consumable
electrode inert gas shielded arc welding is preferred method.
(5) Heat Treatment
AL5052
cannot be hardened by means of heat treatment. It does harden due to cold
working.
(6) Forging
The alloy may be forged in the temperature range of 950 F down to 500 F.
(7) Hot Working
Hot working, as with forging, may be done in the range of 950 F to 500 F.
(8) Cold Working
The alloy cold works readily and may be formed by drawing or spinning. However
the amount of cold work imparted by spinning makes intermediate annealing
necessary.
(9) Annealing
Anneal at 650 F and air cool.
(10) Hardening
Hardens only from cold working.
(11) Other Physical Props
Electrical conductivity 33% of copper.
(12) Other Mechanical Props
Shear strength for O temper is 18 ksi. For cold worked temper H 34 it is 21
ksi.
Typical Application
Commonly used in the manufacture of hydraulic tubes, kitchen
cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, and
appliances. Commonly used in sheet metal work and in sheet metal parts.
Mechanical Properties
Tensile Strength |
196-266MPa |
Yield Strength |
91-127MPa |
Elongation |
10-25 |
Brinell Hardness |
47-68 |
Package:
(1) Standard seaworthy export packing, wooden pallets with plastic protection for coils
(2) The packing for the coil: eye to sky or eye to wall based on the client requirement;
(3) 16-20MT can be loaded into 20FCL.