Chopped Stands for Thermoplastic are based on silane coupling agent and special sizing formulation, compatible with PA,PBT/PET, PP, AS/ABS, PC, PPS/PPO,POM, LCP;
E-Glass Chopped Stands for thermoplastic are know for excellent strand integrity, superior flowability and processing property, delivering excellent mechanical property and high surface quality to its finished product.
Product Features:
● Extremely low resin demand, delivering low viscosity to BMC paste
● High impact strength; High LOI rate
● High strand stiffness; Compatible with rubber
Product Specifications:
● Special specification can be produce according to customer requirements.
Packaging:
Each bag can be taken (15-25kgs). Could also take a big container bag.
Storage:
Unless otherwise specified, It should be stored in a dry, cool and rain-proof area. It is recommended that the room temperature and humidity should be always maintained at 15℃～35℃ and 35%～65% respectively.
E-Glass Chopped Stands for thermoplastic are know for excellent strand integrity, superior flowability and processing property, delivering excellent mechanical property and high surface quality to its finished product.
Product Features:
● Extremely low resin demand, delivering low viscosity to BMC paste
● High impact strength; High LOI rate
● High strand stiffness; Compatible with rubber
Product Specifications:
|
Property
|
Fibre diameter
|
Moisture Content
|
Size Content
|
Chop
|
|
|
(%)
|
(%)
|
(%)
|
(%)
|
|
Mathods
|
IS01888
|
ISO3344
|
ISO1887
|
|
|
3mm
|
±10
|
≤3.0
|
0.1±0.05
|
98
|
|
6mm
|
||||
|
9mm
|
||||
|
12mm
|
Packaging:
Each bag can be taken (15-25kgs). Could also take a big container bag.
Storage:
Unless otherwise specified, It should be stored in a dry, cool and rain-proof area. It is recommended that the room temperature and humidity should be always maintained at 15℃～35℃ and 35%～65% respectively.