| Alloy Or Not: | Is Alloy |
|---|---|
| Shape: | Round |
| Diameter: | all sizes |
| Place of Origin: | China (Mainland) |
Quick Details
Specifications
Chemical Composition:
Be: 1.80-2.00% Co+Ni: 0.20%min. Co+Ni+Fe: 0.60%max. Lead:0.02%max. Cu: Balance (C17200)
Be: 1.80-2.00% Co+Ni: 0.20%min. Co+Ni+Fe: 0.60%max. Lead:0.02-0.06% Cu: Balance (C17300)
Be: 1.60-1.79% Co+Ni: 0.20%min. Co+Ni+Fe: 0.60%max. Cu: Balance (C17300)
Be: 0.20-0.60% Ni: 1.40-2.20% Cu: Balance (C17510)
Be: 0.40-0.70% Co:2.40-2.70% Cu: Balance (C17500)
Note: Copper plus additions equal 99.5% minimum.
Be: 1.80-2.00% Co+Ni: 0.20%min. Co+Ni+Fe: 0.60%max. Lead:0.02-0.06% Cu: Balance (C17300)
Be: 1.60-1.79% Co+Ni: 0.20%min. Co+Ni+Fe: 0.60%max. Cu: Balance (C17300)
Be: 0.20-0.60% Ni: 1.40-2.20% Cu: Balance (C17510)
Be: 0.40-0.70% Co:2.40-2.70% Cu: Balance (C17500)
Note: Copper plus additions equal 99.5% minimum.
Typical Physical Properties:
Density (g/cm3): 8.36 Elastic Modulus (kg/mm2 (103)): 13.10 Thermal Expansion Coefficient (m/m/°C): 17 x 10-6Thermal Conductivity (W/(m.k)): 105 Melting Range (°C): 870-980 (C17200/C17300)
Density (g/cm3): 8.41 Elastic Modulus (kg/mm2 (103)): 13.10 Thermal Expansion Coefficient (m/m/°C): 17 x 10-6
Thermal Conductivity (W/(m.k)): 105 Melting Range (°C): 870-980 (C17000)
Density (g/cm3): 8.83 Elastic Modulus (kg/mm2 (103)): 13.80 Thermal Expansion Coefficient (m/m/°C): 18 x 10-6
Thermal Conductivity (W/(m.k)): 240 Melting Range (°C): 1030-1080 (C17510)
Density (g/cm3): 8.83 Elastic Modulus (kg/mm2 (103)): 13.80 Thermal Expansion Coefficient (m/m/°C): 18 x 10-6
Thermal Conductivity (W/(m.k)): 240 Melting Range (°C): 1010-1050 (C17500)