introducation
Ceramic fibre is made from well chosen aluminum ore which go through high temperature melting in molybdenum wire furnace, vertical spinneret, selection by wind to remove slag, organic coupling and high speed cutting .It has features of good toughness, high temperature resistance, uniform dispersion and low shot content. It can meet high performance requirement of variety of good braking and sealing material.
Technical date
|
Appearance |
Mosh Hardness |
Diameter |
Length |
|
white fibre |
4 |
4-10μm |
300-1000μm |
|
Specific Gravity |
Loss on Ignition |
Shot Content(Above 60meshes) |
Shot Content(Below 100meshes) |
|
0.20-1.92g/cm3 |
<1.5% |
<2.0% |
<6.0% |
|
Strength in Tension |
Al2O3 |
SiO2 |
Fe2O3 |
|
1400-1600MPa |
46.0% |
>=50.0% |
<=1.0% |
Application
Brake pads