Before The Curing 

Appearance	White Paste
Tack Free Time	≤10 (min)
Extrudability	5~11 (g/s,25℃)
Cure Time	3~7(d)

After the curing 

Relative Density	1.40~1.45 (g/cm3)
Tensile Strength	≥2.5 (MPa)
Break Elongation	≥500 (%)
Shear Strength	≥2.0 (MPa)
Hardness	45~55 (Shore A)
The Temperature Range	-60~200 (℃)
Volume Resistivity	2.6×1015 (Ω·CM)
Dielectric Strength	20 (kV/·mm)
Dielectric Constant	3.12
Flame Retardant Grade	UL94 HB

Sample: 300mL / tube, 25tubes / box. 

NOTE

 

After operating, the rest of glue must be sealed to store , and tightened the cap immediately. when using it in the next time, if there is a little crust in sealed place, to remove it and it will not affect the normal application. the process of storage , the canal orifices may appear the phenomenon of the curing, to clean it then it can be used again, and the performance of product is not affected.