| Strength Grade(Mpa): | 62.5-92.5 |
|---|---|
| Heat of Hydration: | Low-Heat |
| Hardening Feature: | Extra Rapid Hardening |
| Type: | Cement Clinker |
| Main Raw Material: | C4A3SC2S |
| Feature: | Acid-Proof,Decorative,Expansive,Sulfate Resistant |
| Color: | Grey |
| Model Number: | CSA cement clinker |
| Brand Name: | polar bear |
| Place of Origin: | China (Mainland) |
| Al2O3: | 33~36% |
| Product standard: | Q/TBJX09-2015 |
| Certification: | ISO 9001,14001 |
| Samples: | available |
| OEM: | available |
| technical support: | available |
| enquiry: | available |
| packing customize: | available |
| Appearance: | powder |
Quick Details
Specifications
cement price,clinker price,csa cement clinker price,csa cement clinker 82.5
application short time urgent project
main raw material calcium sulpho aluminate
main properties high early strength
usage 6%-12% to ordinary cement
construction agent concrete anti-crackagent
CSA cement
CSA cement is not a cement,it is a pure cement clinker, also called CSA binder in field of china construction building materials. In fact, it is a hydraulic binder based on Calcium sulphoalumniate rather than portland cement which consist of calcium silicate or alumina cement which consist of calcium aluminate. Its main efficient content is ettringite. It can be gained after reaction with each other and the volume is twice than the mixture of limestone, bauxite, gypsum ect. Due to 85% of ettringite is formated in early period, it has good durability and short stable time. It also can be used as concrete additive agent like high early strength agent, anti-crack waterproofing agent, anti-freeze agent, rapid hardening agent ect. Besides, it has good adaption to other cement, chemical auxiliary agent, mineral materials ect.
main constituent(%)
|
Type |
SiO2 |
Al2O3 |
Fe2O3 |
CaO |
MgO |
TiO2 |
SO3 |
|
Csa binder 72.5 |
<=10.5 |
>=34 |
<=3.5 |
39.5-42.0 |
<=3.5 |
1.0-2.0 |
>=7.5 |
|
Csa binder 82.5 |
<=8.5 |
>=35 |
<=3.5 |
40.0-43.0 |
<=3.5 |
1.0-2.0 |
>=8.0 |
|
Csa binder 92.5 |
<=7.0 |
>=36 |
<=2.5 |
39.5-42.0 |
<=3.5 |
1.0-2.0 |
>=9.0 |
Finess:
specific surface area: according to standard GB/T 8074-1987
Usual range:360~430m2/kg
Specification limit:>36m2/kg
Physcial properties:
l Setting time determined at 20 using Vicat needle, according to GB/T 1346-2001
l Mechanical strength at 20 , 95% relative humidity.
Mortar according to JC933-2003
|
Initial Set |
Final Set |
|
|
Specification limit |
>25 minutes |
<180 minutes |
|
Item |
Compressive strength(mpa) |
Flexural strength(mpa) |
||||
|
Type |
1d |
3d |
7d |
1d |
3d |
7d |
|
Csa binder 72.5 |
>=50.0 |
>=65.0 |
>=75.0 |
>=6.0 |
>=8.0 |
>=9.0 |
|
Csa binder 82.5 |
>=50.0 |
>=75.0 |
>=85.0 |
>=7.0 |
>=9.0 |
>=10.0 |
|
Csa binder 92.5 |
>=60.0 |
>=85.0 |
>=95.0 |
>=8.0 |
>=10.0 |
>=11.0 |
These properties are applied to obtain a wide range of products:
l Fast setting cements
l Rapid hardening mortars
l Tile adhesives
l Self-leveling compounds
l Non-shrink grouts
l Water stopping mortars
l etc.