Alloy Or Not: | Is Alloy |
---|---|
Special Pipe: | API Pipe |
Surface Treatment: | Galvanized |
Certification: | API |
Technique: | Hot Rolled |
Application: | Oil Pipe |
Secondary Or Not: | Non-secondary |
Place of Origin: | China (Mainland) |
Section Shape: | Square |
Thickness: | 12-545 mm |
Standard: | API |
Standard: | API 5DP |
Quick Details
Specifications
Size designation |
Calculated weight |
Tool joint designation |
Calculated weight |
grade |
Wall thickness |
Upset ends |
||
in |
1b/ft |
Kg/m |
in |
mm |
||||
2 3/8 |
6.65 |
NC26 |
6.26 |
9.32 |
E.X.G.S |
0.28 |
7.11 |
EU |
2 7/8 |
10.4 |
NC31 |
9.72 |
14.48 |
E.X.G.S |
0.362 |
9.19 |
EU |
3 1/2 |
13.3 |
NC38 |
12.31 |
18.34 |
E.X.G.S |
0.368 |
9.35 |
EU |
3 1/2 |
15.5 |
NC38,NC40 |
14.63 |
21.79 |
E.X.G.S |
0.449 |
11.4 |
EU |
4 |
14 |
NC40,NC46 |
12.93 |
19.26 |
E.X.G.S |
0.33 |
8.38 |
IU,EU |
4 1/2 |
16.6 |
NC46,NC50 |
14.98 |
22.31 |
E.X.G.S |
0.337 |
8.56 |
EU,IEU |
4 1/2 |
20 |
NC46,NC50 |
18.69 |
27.84 |
E.X.G.S |
0.43 |
10.92 |
EU,IEU |
5 |
19.5 |
NC50,NC52 |
17.93 |
26.71 |
E.X.G.S |
0.362 |
9.19 |
IEU |
5 |
25.6 |
NC50,5 1/2FH |
24.03 |
35.79 |
E.X.G.S |
0.5 |
12.7 |
IEU |
5 1/2 |
21.9 |
5 1/2FH |
19.81 |
29.51 |
E.X.G.S |
0.361 |
9.17 |
IEU |
5 1/2 |
24.7 |
5 1/2FH |
22.54 |
33.57 |
E.X.G.S |
0.415 |
10.54 |
IEU |
6 5/8 |
25.2 |
6 5/8FH |
22.19 |
33 |
E.X.G.S |
0.33 |
8.387 |
IEU |
6 5/8 |
27.7 |
6 5/8FH |
24.21 |
41 |
E.X.G.S |
0.362 |
9.19 |
IEU |
Chemical Composition(%):
Grade |
Chemical composition |
|
P |
S |
|
E75 |
<0.015 |
<0.003 |
X95 |
<0.015 |
<0.003 |
G105 |
<0.015 |
<0.003 |
S135 |
<0.015 |
<0.003 |
Tool joint |
<0.015 |
<0.003 |
Mechanical Properties:
Pipe body |
Grade |
Yield strength |
Tensile strength |
Elongation |
Hardness |
Full size charpy impact test(J) |
||||||
min |
max |
min |
min |
|||||||||
Psi |
MPa |
Psi |
MPa |
Psi |
MPa |
HBW |
HRC |
Average |
Single |
|||
E75 |
75000 |
517 |
105000 |
724 |
100000 |
689 |
625000A0.2/U0.9 |
- |
- |
80 |
65 |
|
X95 |
95000 |
655 |
125000 |
862 |
105000 |
724 |
- |
- |
80 |
65 |
||
G105 |
105000 |
724 |
135000 |
931 |
115000 |
793 |
- |
- |
80 |
65 |
||
S135 |
135000 |
931 |
165000 |
1138 |
145000 |
1000 |
- |
- |
80 |
65 |
||
Weld zone |
Tool joint |
120000 |
827.4 |
- |
- |
140000 |
965.3 |
=13% |
=285 |
- |
80 |
65 |
E75 |
75000 |
517 |
- |
- |
100000 |
689 |
- |
37 |
40 |
27 |
||
X95 |
88000 |
609 |
- |
- |
103000 |
712 |
- |
37 |
40 |
27 |
||
G105 |
95000 |
655 |
- |
- |
105000 |
724 |
- |
37 |
40 |
27 |
||
S135 |
105000 |
724 |
- |
- |
115000 |
37 |
40 |
27 |
Drill Collars are integral heavy-wall joints that are manufactured from a solid bar of modified alloy steel. The solid bars are quenched and tempered to obtain the required mechanical properties, then trepanned, drifted and threaded. Drill collars are furnished as slick or spiraled in 30 or 31 foot lengths.
Slick drill collars are supplied with the mill as-rolled surface finish. Spiraled drill collars have grooves machined in the outside surface. The spiral grooves promote even flow of drilling fluid around the collar diameter, equalizing pressure and reducing the occurrence of differential sticking.