| Type: | Alloy Steel Bar |
|---|---|
| Special Use: | Mold Steel |
| Application: | Die Steel Bar |
| Technique: | Forged |
| Model Number: | AISI O1 |
| Brand Name: | Kangheng |
| Place of Origin: | China (Mainland) |
| Dimensions: | 16-500mm |
| Standard: | AISI,ASTM,BS,DIN,GB,JIS |
| Steel Grade: | Forged Round Steel AISI O1 |
| Product Name: | Cold Working Alloy Forged Die Steel AISI O1 |
| Surface treatment: | Black/Grinded/Machined/Turned |
| Production route: | EF/EAF+LF+VD/ESR |
| Quality inspection: | UT, Chemical test, Microstructure, Physical properties etc. |
| UT test standard: | SEP1921-84 class3 C/c to D/d |
| Certification: | ISO9001 |
| Service: | Free Sample and 24 Hours Online |
| Tolerance: | 0/+1.0mm(turned) -0/+5.0mm(black) |
| Delivery Condition: | Hot Forged or Rough Machined |
| Heat Treatment: | Annealing/Quenching/Tempering |
Quick Details
Specifications
Cold Working Alloy Forged Die Steel AISI O1
| Steel Grade | ||||||
| GB | DIN | W-Nr | AISI | JIS | BOHLER | Ss14 |
| 9CrWmn | 100MnCrW4 | 1.2510 | O1 | SKS3 | K460 | 2140 |
| Size of AISI O1 (can be sustomized) | ||||
| Round bar | Diameter(mm): | Hot Forgeed:φ50-500 | Length(mm):2500-5800 | |
| Hot Rolled:φ≤50 | ||||
| Steel plate | Thickness(mm): | Hot Forged: ≥20 | Width(mm): 20-810 | |
| Hot Rolled: ≤20mm | ||||
| Chemical Composition | |||||||
| C | Si | Mn | P | S | Cr | Ni | W |
| 0.85-0.95 | ≤0.40 | 0.90-1.20 | ≤0.030 | ≤0.030 | 0.50-0.80 | ≤0.25 | 0.50-0.80 |
| GB 9CRWMN/DIN 100MNCRMOV5/W-Nr 1.2510/ASTM O1/JIS SKS3/BOHLER K460/Ss14 2140 | |||
| Characteristics: | |||
| 1.Low alloy cold work mold steel; | |||
| 2.Good hardenability and wear resistance; | |||
| 3.Quenching deformation is small; | |||
| 4.High strength. | |||
| Applications: | |||
| 1.For making small cross section,complex shape and high precision cold-puching mould; | |||
| 2.For making sheet stamping die ,jewelry embossing dies,etc; | |||
| 3.For overall hardening typeplastic mold; | |||
| 4.For thermoset plastic forming mold,need high wear resistance ang high strength . |