High alumina cement
High alumina cement, also known as alumina cement, refractory cement, aluminate cement, collectively referred to as aluminate cement, is with bauxite and limestone as raw material, the calcination of calcium aluminate as main ingredients, alumina content is about 50% of the clinker, grinding is made of water hydraulic cementitious materials. High alumina cement is often yellow or brown, there is a gray. With rapid hardening, early strength, corrosion resistance, resistance to high temperature of the water hydraulic cementitious materials; it is a kind of high quality building materials and a cementitious powder shaped refractory material, in the metallurgy, building materials, petrochemical, electricity, food and other industries has a widely used.
Production requirement of high alumina cement
1, fineness: the finer the cement particles, the larger the surface area, the faster the more full hydration, early and late strength are higher. State regulations: the specific surface area should be more than 300 square meters / kg, otherwise not qualified.
2, setting time: in order to guarantee in the construction have plenty of time to finish the mixing, transportation, molding, and other various process, cement and its initial setting time shoulds not be too short; after the completion of construction, hope cement as soon as possible hardening and strength, therefore the end coagulation time shoulds not be too long. Portland cement at the beginning of the first set of time shall not be earlier than 45 minutes, the final setting time shall not be later than 390 minutes.
3, volume stability: cement paste in the coagulation process of volume change uniformity called the volume stability of cement. If the volume change is not uniform, that is, the volume stability is poor, prone to warping and cracking, reduce the quality of the project and even the accident.
4, refractory cement baking refractory cement lining baking, must pay attention to the following matters:
1) at room temperature 350 degrees, the most likely to cause local burst, to pay special attention to the slow baking. If there are still a lot of steam after the 350 degree heat, still should slow down the speed of heating.
2) in the condition of bad ventilation, water vapor is not easy to discharge, to properly extend the heat preservation time.
3) when using heavy oil for baking, to prevent oil sprayed on the surface of the furnace lining, to prevent local burst.
4) when using wood baking, direct contact with the flame is often caused by local heating too fast, should be protected.
5) to the new cast of refractory cement, at least through the 3D can be carried out after baking.
6) for refractory cement lining should also slow cooling, avoid forced ventilation.
High alumina cement application
High alumina cement and sulphoaluminate cement refractory cement, equivalent to the cement 625#. Because of its excellent fast setting, high strength, resistance to high temperature characteristics of that day intensity can reach 80% and refractoriness up to 1450 degrees, refractory concrete strength up to 55MPa, is one of the industrial furnace engineering excellent high temperature binder material.
High alumina cement, also known as alumina cement, refractory cement, aluminate cement, collectively referred to as aluminate cement, is with bauxite and limestone as raw material, the calcination of calcium aluminate as main ingredients, alumina content is about 50% of the clinker, grinding is made of water hydraulic cementitious materials. High alumina cement is often yellow or brown, there is a gray. With rapid hardening, early strength, corrosion resistance, resistance to high temperature of the water hydraulic cementitious materials; it is a kind of high quality building materials and a cementitious powder shaped refractory material, in the metallurgy, building materials, petrochemical, electricity, food and other industries has a widely used.
Production requirement of high alumina cement
1, fineness: the finer the cement particles, the larger the surface area, the faster the more full hydration, early and late strength are higher. State regulations: the specific surface area should be more than 300 square meters / kg, otherwise not qualified.
2, setting time: in order to guarantee in the construction have plenty of time to finish the mixing, transportation, molding, and other various process, cement and its initial setting time shoulds not be too short; after the completion of construction, hope cement as soon as possible hardening and strength, therefore the end coagulation time shoulds not be too long. Portland cement at the beginning of the first set of time shall not be earlier than 45 minutes, the final setting time shall not be later than 390 minutes.
3, volume stability: cement paste in the coagulation process of volume change uniformity called the volume stability of cement. If the volume change is not uniform, that is, the volume stability is poor, prone to warping and cracking, reduce the quality of the project and even the accident.
4, refractory cement baking refractory cement lining baking, must pay attention to the following matters:
1) at room temperature 350 degrees, the most likely to cause local burst, to pay special attention to the slow baking. If there are still a lot of steam after the 350 degree heat, still should slow down the speed of heating.
2) in the condition of bad ventilation, water vapor is not easy to discharge, to properly extend the heat preservation time.
3) when using heavy oil for baking, to prevent oil sprayed on the surface of the furnace lining, to prevent local burst.
4) when using wood baking, direct contact with the flame is often caused by local heating too fast, should be protected.
5) to the new cast of refractory cement, at least through the 3D can be carried out after baking.
6) for refractory cement lining should also slow cooling, avoid forced ventilation.
High alumina cement application
High alumina cement and sulphoaluminate cement refractory cement, equivalent to the cement 625#. Because of its excellent fast setting, high strength, resistance to high temperature characteristics of that day intensity can reach 80% and refractoriness up to 1450 degrees, refractory concrete strength up to 55MPa, is one of the industrial furnace engineering excellent high temperature binder material.