Properties:

Quartz roller good surface smoothness, not easy to scratch glass

High Compressive Strength, Flexural Strength & Impact Strength at high temperature.

Good wear resistance

Low thermal expansion coefficient

Strong thermal shock stability

No deformation under high temperature

Long service life, The reliable axle neck joint technology(anti-loose technology)

High economic efficiency

 

Application:

Fused silica ceramic roller is ideal substitute for graphite rolls and ceramic coating rolls, prevent oxidation and dross build-up, carrying and transmitting glass in glass horizontal tempering furnace and annealing kilns.

 

Index	Unit	Data
SiO2 content	%	≥99.7
Bulk Density	g/cm3	>1.95
Apparent Porosity	%	7-11
Compressive Strength	Mpa	≥60
Surface Roughness Ra	um	≤1.6
Diameter Tolerance	mm	±0.05
Circular Runout	mm	≤0.08
High-temperature Bending Strength	Mpa	≥30
Coefficient of Thermal Expansion	×10-6/°C	<0.6