| Type: | Geocells |
|---|---|
| Material: | HDPE |
| Brand Name: | Dongkai |
| Type: | geocell |
| color: | black |
| length: | 4-12m |
| Place of Origin: | China (Mainland) |
Quick Details
Specifications
Plastic HDPE Geocell
|
Test method |
Result |
Material |
---- |
HDPE |
Minimum Carbon black |
ASTM D 1603 |
2% |
Sheet Thickness (smooth) |
ASTM D 5199 |
1.10mm |
Sheet Thickness (textured ) |
ASTM D 5199 |
1.50mm |
Denisity |
ASTM D 1505 |
0.94g/cm3 |
Geocell is a lightweight and flexible three-dimensitional,expandable panels made of high-density polythylene(HDPE) sheets which are ultrasonically bonded together to make to be an extremely strong configuration. Geocell system can be filled with concrete,sand,soil ect.
Items |
Welding sEam peel Strength (N) |
Welding Distance(mm) |
Cell Height |
Expand cell (mm) |
THickness(mm) after texture |
Tensile Yield Strength |
TGLG75-330 |
>1060N |
330 |
75 |
241x208 |
1.5~1.6 |
≥23MPa |
TGLG100-330 |
>1420N |
330 |
100 |
241x208 |
1.5~1.6 |
≥23MPa |
TGLG150-330 |
>2130N |
330 |
150 |
241x208 |
1.5~1.6 |
≥23MPa |
TGLG50-400 |
>710N |
400 |
50 |
292x252 |
1.5~1.6 |
≥23MPa |
TGLG100-400 |
>1420N |
400 |
100 |
292x252 |
1.5~1.6 |
≥23MPa |
TGLG150-400 |
>2130N |
400 |
150 |
292x252 |
1.5~1.6 |
≥23MPa |
TGLG200-400 |
>2840N |
400 |
200 |
292x252 |
1.5~1.6 |
≥23MPa |
Long term seam peel strength test |
Long term seam peel-strength test shall be performed on all resin or pre-manufactured sheet or strips.A 4.0 in (100mm) wide seam sample shall support a 160 lb(72.5kg)load for a period of 168 hours(7days) minimum in a temperature-controlled environment undergoing a temperature change on a 1-hour cycle from ambient room to 130F(54C).Ambient room temperature is per ASTM E 41 | |||||
10,000 hours seam peel strength certification |
PResto shall provide data showing that the high-density polyethylene resin used to produce the GEOCELL section has been tested using an appropriate number of seam samples and varying loads to generate data indicating that the seam peel strength shall survive a loading of at least 209lbf(95kg) for a minimum of 10,000 hours | |||||