Application: | Paper |
---|---|
K2O Content (%): | 0.05 |
Whiteness: | 95 |
Al2O3 Content (%): | 36 |
Fe2O3 Content (%): | 0.39 |
TiO2 Content (%): | 0.045 |
Moisture Content (%): | 0.4 |
SiO2 Content (%): | 55 |
Technique: | Calcined Kaolin |
Type: | Powder |
Model Number: | JH-601 |
Place of Origin: | China (Mainland) |
PH: | 5.6 |
Quick Details
Specifications
Calcined Kaolin Clay Is a kind of nonmetallic minerals, is a kind of kaolinite mineral clay and clay rock. the pure Kaolin Powder is white and fine, soft soil, it has good plasticity and fire resistance.Its mineral composition mainly consists of kaolinite, halloysite, hydromica, illite and montmorillonite, quartz and feldspar mineral composition.Kaolin Clay application is very extensive, mainly used for paper making, ceramics and refractory materials, secondly used in paints, rubber filler, enamel glaze and white cement raw material, a few used in plastics, paint, paint, grinding wheel, pencil, daily cosmetics, soap, pesticide, medicine, textile, oil, chemical industry, building materials, and so on!
Calcined Kaolin Clay Technology Data Sheet:
Project |
Typical target |
Remark |
Appearance |
White powder |
Visual inspection |
ISO Whiteness (%) |
87-88 |
Wavelength 457nm Whiteness meter |
Particle size (-2 um%) |
50-60 |
Centrifugal settling type particle size meter |
Average particle diameter |
<1.0 |
Centrifugal settling type particle size meter |
Moisture(%) |
3 |
Constant temperature 105 2h |
PH |
4-6 |
10% Aqueous solution |
Residue (+325%) |
0.02 |
Washing |
|
40-50 |
GB/T 14563-93 |
Jiahe Calcined Kaolin Clay
Test Items | Typical Value | Test Result | ||||
Whiteness(R457) | 92-98 | 92 | ||||
Particle Size(-5m,%) | 95-98 | 96 | ||||
Screen Residue(325Mesh,%) | 0-0.5 | 0.2 | ||||
Moisture(105,%) | 0-0.5 | 0.5 | ||||
PH value(10%, Solid) | 5.5-7.5 | 5.9 | ||||
Bulk Density(Kg/L) | 0.3-0.5 | 0.4 | ||||
Specific Gravity(g/cm) | 2.65-2.75 | 2.65 | ||||
Oil Absorption(g/100g) | 50-60 | 52 | ||||
Hegman | 4 - 5 | 4.2 | ||||
SiO(Wt,%) | 52-56 | 52 | ||||
AlO (Wt,%) | 42-46 | 45 | ||||
FeO(Wt,%) | 0-0.8 | 0.5 | ||||
TiO(Wt,%) | 0-1.2 | 1 | ||||
CaO(Wt,%) | 0-0.5 | 0.3 | ||||
MgO(Wt,%) | 0-0.3 | 0.2 | ||||
KO(Wt,%) | 0-0.1 | 0.1 | ||||
NaO(Wt,%) | 0-0.2 | 0.1 | ||||
MoO(Wt,%) | 0-0.004 | 0.002 | ||||
LOI(Wt,%) | 0-0.5 | 0.3 | ||||
Quartz(Wt,%) | 0-1.2 | 1 | ||||
Melting point() | 1580-1780 | 1689 |