Performance Properties:

 

1. Shore Hardness (HA): 65 (50)

 

2. Tensile Strength (Mpa): 15 (9)

 

3. Elongation Ratio %: 482 (400)

 

Hot Air Aging Test @ (100 168h)

 

4. Hardness Change: 3.5 (-5~+10)

 

5. Tensile Strength Change Rate %: 12.7 (25)

 

6. Elongation Ratio Change Rate %: 18 (40)

 

Hot Air Aging Test @ (70 48h)

 

7. Recovery Rate after Hot Air Aging (Da) %: 31.5 (3 Class, 50% Da60%)

 

8. Shore Hardness Change (-20~0): 5.1 (10)

 

9. Shore Hardness Change (0~23): 0.2 (10)

 

10. Shore Hardness Change (23~70): 2.7 (10)

 

11. Low Temperature Brittleness Temperature (-40): NO Brittle @-40

 

12. High Temperature Brittleness Temperature (220): NO Brittle @220

 

13. Volume Resistivity cm: 1.5*1013cm (1.1*1013cm)

 

14. Surface Resistivity: 1.2 (2.0)

 

15. Puncture Strength KV/mm: 10~220KV/mm

 

16. Ozone Aging Resistance Properties (500pphm Elongation 20% @40 48h): NO Fracturing on Surface