| Type: | Waterproof Membrane |
|---|---|
| Brand Name: | Tianhai |
| Type: | smooth |
| Color: | black |
| Thickness: | 1.0mm |
| Length: | 100m |
| Place of Origin: | China (Mainland) |
| color: | black |
| quality: | GM13 |
| function: | waterproofing |
| certificate: | ISO |
Quick Details
Specifications
Shandong Tianhai HDPE geomembrane is the low permeable synthetic membrane liner and Geotechnical engineering materials which is widely used for solid waste Containment, mining and water containment applications. As the leading Geomembranes manufacturer, wholesaler, supplier and exporter, Shandong Tianhai has Been dedicated to supplying one stop geomembranes and services to worldwide Customers since its foundation in 2002. Our innovative, high quality Geomembranes include Smooth HDPE Liner, Textured HDPE Geomembrane, Composite Geomembrane Liner, HDPE liner, pond liner and geotextile membranes, etc, which Are your best choice for environmental, civil and industrial applications. All Shandong Tianhai brand HDPE geomembranes had been certificated by the ISO9001, ISO14001, TUV, TRI, BTTG,CE and SGS certificates etc. Product innovation, Quality assurance and customer satisfaction are our long term commitment to our Worldwide customers.
HDPE fish pond liner specification data
Smooth HDPE geomembrane-GM13(ASTM) technical data | |||||||||||
Properties |
Test Method |
Test Value | |||||||||
0.75 mm |
1.00 mm |
1.25 mm |
1.50 mm |
2.00 mm |
2.50 mm | ||||||
Thickness (min. ave.) lowest individual of 10 values |
D5199 |
Nom -10% |
Nom -10% |
Nom -10% |
Nom -10% |
Nom -10% |
Nom -10% | ||||
Density (min.) |
D 1505/D 792 |
0.94 |
0.94 |
0.94 |
0.94 |
0.94 |
0.94 | ||||
Yield Strength |
D 6693 |
11 kN/m |
15 kN/m |
18 kN/m |
22 kN/m |
29 kN/m |
37 kN/m | ||||
Break Strength |
20 kN/m |
27 kN/m |
33 kN/m |
40 kN/m |
53 kN/m |
67 kN/m | |||||
Yield Elongation |
12% | ||||||||||
Break Elongation |
700% | ||||||||||
Tear Resistance (min. ave.) |
D 1004 |
93 N |
125 N |
156 N |
187 N |
249 N |
311 N | ||||
Puncture Resistance (min. ave.) |
D 4833 |
240 N |
320 N |
400 N |
480 N |
640 N |
800 N | ||||
Stress Crack Resistance (2) |
D 5397 |
300 hr. | |||||||||
Carbon Black Content - % |
D 4218 |
2.0-3.0% | |||||||||
Oxidative Induction Time (OIT) (min. ave.) |
|
|
|
|
|
|
| ||||
(a) Standard OIT |
D 3895 |
100 min. | |||||||||
(b) High Pressure OIT |
D 5885 |
400 min. | |||||||||
Oven Aging at 85C |
|
|
|
|
|
|
| ||||
(a) Standard OIT (min. ave.) - % retained after 90 days |
D 3895 |
55% | |||||||||
(b) High Pressure OIT (min. ave.) - % retained after 90 days |
D 5885 |
80% | |||||||||
UV Resistance |
|
|
|
|
|
|
| ||||
High Pressure OIT (min. ave.) - % retained after 1600 hrs |
D 5885 |
50% | |||||||||