| Type: | Geomembranes |
|---|---|
| Material: | EVA,HDPE,LDPE,LLDPE,PVC |
| Brand Name: | Tianhai |
| Type: | smooth |
| thickness: | 1.0mm |
| color: | black |
| Place of Origin: | China (Mainland) |
| color: | black |
| quality: | GM13 |
| function: | waterproofing |
| certificate: | ISO |
| sample: | yes |
Quick Details
Specifications
Geomembranes are impermeable geosynthetics that, until recently, were mainly used as canal and pond liners. however, Modern technology has broadened liner applications to include landfills, Wastewater treatment lagoons, oil and gas exploration (including hydraulic Fracturing or "fracking"), aquaculture, irrigation ponds and Remediation. In many of these applications, a nonwoven geotextile is used as a Cushion to protect the geomembrane. In general, geomembrane liners offer Excellent puncture resistance and can withstand a wide range of chemicals and Temperatures. They are also highly flexible and conform well to the subgrade.
HDPE pond liner specification data
Smooth HDPE geomembrane-GM13(ASTM) technical data | |||||||||||
Properties |
Test Method |
Test Value | |||||||||
0.75 mm |
1.00 mm |
1.25 mm |
1.50 mm |
2.00 mm |
2.50 mm | ||||||
Thickness (min. ave.) lowest individual of 10 values |
D5199 |
Nom -10% |
Nom -10% |
Nom -10% |
Nom -10% |
Nom -10% |
Nom -10% | ||||
Density (min.) |
D 1505/D 792 |
0.94 |
0.94 |
0.94 |
0.94 |
0.94 |
0.94 | ||||
Yield Strength |
D 6693 |
11 kN/m |
15 kN/m |
18 kN/m |
22 kN/m |
29 kN/m |
37 kN/m | ||||
Break Strength |
20 kN/m |
27 kN/m |
33 kN/m |
40 kN/m |
53 kN/m |
67 kN/m | |||||
Yield Elongation |
12% | ||||||||||
Break Elongation |
700% | ||||||||||
Tear Resistance (min. ave.) |
D 1004 |
93 N |
125 N |
156 N |
187 N |
249 N |
311 N | ||||
Puncture Resistance (min. ave.) |
D 4833 |
240 N |
320 N |
400 N |
480 N |
640 N |
800 N | ||||
Stress Crack Resistance (2) |
D 5397 |
300 hr. | |||||||||
Carbon Black Content - % |
D 4218 |
2.0-3.0% | |||||||||
Oxidative Induction Time (OIT) (min. ave.) |
|
|
|
|
|
|
| ||||
(a) Standard OIT |
D 3895 |
100 min. | |||||||||
(b) High Pressure OIT |
D 5885 |
400 min. | |||||||||
Oven Aging at 85C |
|
|
|
|
|
|
| ||||
(a) Standard OIT (min. ave.) - % retained after 90 days |
D 3895 |
55% | |||||||||
(b) High Pressure OIT (min. ave.) - % retained after 90 days |
D 5885 |
80% | |||||||||
UV Resistance |
|
|
|
|
|
|
| ||||
High Pressure OIT (min. ave.) - % retained after 1600 hrs |
D 5885 |
50% | |||||||||