Shop sign:ZG-P-6689/ZG-I-5002
 
1.Characteristics:High hardness,high density,smooth surface,good resilience PU resin for tire.
2.Application:Applicable for the production of tire.
3. Typical properties of PU Resin

Name of products	Appearance	Viscosity (Pas/50C)	Density (g/cm3/40C)	Package (kg)
ZG-P-6689	White or pale yellow, liquid, no foreign material	0.60-1.20	1.16-1.20	18
ZG-I-5002	Transparent liquid, no foreign material	0.30-0.50	1.18-1.20	20

Reference shipments ratio: A/B=30/25(barrel)
4. Catalysts and auxiliary agents:
ZG-P-6689/ZG-AC-2/water =18kg/280g/80g
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
5. (Molding conditions & physical properties):

Reactivity	Technical index	Test item	Reference physical properties
Reference ratio P+C/I	100/120	Molded density of sole (g/cm3)	0.35-0.85
Using temperature(C)	A material: 45-50; B material:38-42	Hardness (type A)	70-90
Cream time(s)	5-9	Tensile strength(MPa)	6.0-8.0
Rise time(s)	30-45	Elongation(%)	350-450
Metal mold temperature (C)	45-55	DIN abrasion resistance(mm3)	<=500
Demould time (min)	2.5-4	Free foam density (g/cm3)	0.25-0.40
		Folding endurance (room temperature) (40,000 gap length mm)	<8