Shop sign: ZG-P-8086D/ZG-I-9823D

Super high-hardness and super low-density PU Resin for shoe sole
1. Characteristic: Super-high hardness, super-low density.
2. Application: Applicable to the production of shoe soles for both men and women
3. Typical properties of PU Resin

Name of products	Appearance	Viscosity (Pas/50C)	Density (g/cm3/40C)	Package (kg)
ZG-P-8086D	, White or pale yellow, liquid, no foreign material	0.30-0.70	1.16-1.20	18
ZG-I-9823D	Transparent liquid, no foreign material	0.05-0.20	1.18-1.20	20

Reference shipments ratio: A/B=28/25(barrel)
4. Catalysts and auxiliary agents:
ZG-P-8086D/ZG-AC-2/water =18kg/350g/70-150g   
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
5. (Molding conditions & physical properties):

Reactivity	Technical index	Test item	Reference physical properties
Reference ratio P+C/I	100/110	Molded density of sole (g/cm3)	0.30~0.50
Using temperature(C)	A material: 45-50; B material: 38-42	Hardness (type A)	60~90
Cream time(s)	6~9	Tensile strength(MPa)	-
Rise time(s)	30~45	Elongation(%)	-
Material mold temperature (C)	55~65	NBS abrasion resistance(%)	≥10%
Demould time (min)	5.0~7.0	Free foam density (g/cm3)	0.12~0.15
		Folding endurance (room temperature) (40,000 gap length mm)	-