Shop sign:ZG-P-5005/ZG-I-5002
 
1.Characteristics:Medium to low hardness,medium to high density,good resilience PU resin for shoe sole.
2.Application:Applicable for the production of shoe sole with the upper and slippers for men and women.
3. Typical properties of PU Resin

Name of products	Appearance	Viscosity (Pas/50C)	Density (g/cm3/40C)	Package (kg)
ZG-P-5005	White or pale yellow, liquid, no foreign material	0.40-0.70	1.16-1.20	18
ZG-I-5002	Transparent liquid, no foreign material	0.10-0.40	1.18-1.20	20

Reference shipments ratio: A/B=30/25(barrel)
4. Catalysts and auxiliary agents:
ZG-P-5005/ZG-AC-2/water =18kg/300g/60g
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
5. (Molding conditions & physical properties):

Reactivity	Technical index	Test item	Reference physical properties
Reference ratio P+C/I	100/100	Molded density of sole (g/cm3)	0.32-0.55
Using temperature(C)	A material: 45-50; B material:38-42	Hardness (type A)	20-60
Cream time(s)	5-9	Tensile strength(MPa)	6.0-8.0
Rise time(s)	30-45	Elongation(%)	250-450
Metal mold temperature (C)	45-55	DIN DIN abrasion resistance(mm3)	<=300
Demould time (min)	2.5-4	Free foam density (g/cm3)	0.15-0.30
		() (4,mm) Folding endurance (room temperature) (40,000 gap length mm)	<8