(Shop sign):ZG-P-6006/ZG-I-1032
 
1.Characteristics:Medium to high hardness,medium to high density PU resin for shoe sole.
2.Application:Applicable for the production of shoe sole with the upper and slippers for men and women.
3. Typical properties of PU Resin

Name of products	Appearance	Viscosity (Pas/50C)	Density (g/cm3/40C)	Package (kg)
ZG-P-6006	White or pale yellow, liquid, no foreign material	0.50-0.70	1.16-1.20	18
ZG-I-1032	Transparent liquid, no foreign material	0.10-0.30	1.18-1.20	20

Reference shipments ratio: A/B=30/25(barrel)

4. Catalysts and auxiliary agents:
ZG-P-6006/ZG-AC-2/water =18kg/200-300g/30-60g Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.

5. (Molding conditions & physical properties):

Reactivity	Technical index	Test item	Reference physical properties
Reference ratio P+C/I	100/79-83	Molded density of sole (g/cm3)	0.28-0.65
Using temperature(C)	A material: 45-50; B material:38-42	Hardness (type A)	60-90
Cream time(s)	5-9	Tensile strength(MPa)	6.0-8.0
Rise time(s)	30-45	Elongation(%)	200-400
Metal mold temperature (C)	45-55	DIN DIN abrasion resistance(mm3)	<=500
Demould time (min)	2.5-4	Free foam density (g/cm3)	0.26-0.44
		Folding endurance (room temperature) (40,000 gap length mm)	<8