GPPS (General purpose polystyrene)
General-purpose polystyrene is a thermoplastic resin that is a colorless, odorless, odorless, shiny, transparent beaded or granulated solid. The density is 1.04~1.09, the transparency is 88%~92%, and the refractive index is 1.59~1.60. under the action of stress, birefringence is produced, the so-called stress-optical effect. The melting temperature of the product is 150~180°C, the thermal decomposition temperature is 300°C, the heat distortion temperature is 70~100°C, and the long-term use temperature is 60~80°C.
GPPS is low water absorption, in a wet environment can still maintain its mechanical properties and dimensional stability. Excellent electrical properties, volume resistivity and surface resistivity are high, and independent of temperature, humidity changes, are not subject to corona discharges. Radiation resistance is also very good.
GPPS is low water absorption, in a wet environment can still maintain its mechanical properties and dimensional stability. Excellent electrical properties, volume resistivity and surface resistivity are high, and independent of temperature, humidity changes, are not subject to corona discharges. Radiation resistance is also very good.
Application
Food packingDue to the transparency of GPPS and excellent rigidity, electrical properties and printing performance, especially good hygiene and low cost, it has broad application prospects in food packaging.
Electromechanical industry, instrumentation, communication equipment industry.Instrument housing, lampshade, optical parts, instrument parts;Acid trough, telecommunications parts, high frequency capacitors,etc.
Daily necessities.Bottle caps, containers, decorations, buttons, combs, toothbrushes, soap boxes, cigarette boxes and toys,etc.
Product Parameters
Item |
Test conditions | Test method | Test data | unit |
| Density | ISO 1183:1987 | 1040 | kg/m3 | |
| Water absorption | ISO 62:1999 | <0.1 | % | |
| Melt flow rate | 200°C/5kg | ISO 1133:1997 | 3.8 | Cm3/10min |
| Process shrinkage | ISO 294-4:1997 | 0.4-0.6 | % | |
| Charpy impact strength | 1eU | ISO 179:1993 | 15 | kj/m2 |
| Tensile modulus | 1mm/min | ISO 527-2:1993 | 3300 | MPa |
| Elongation | 50mm/min | ISO 527-2:1993 | 3 | % |
| Tensile strength at break | 50mm/min | ISO 527-2:1993 | 55 | MPa |
| Ball indentation hardness H | 358N/30s | ISO 2039-1:1993 | 150 | N/mm2 |
| Bending strength | 2mm/min | ISO 178:1993 | 100 | MPa |
| HDT | 1.8MPa | ISO 75-2:1993 | 84 | °C |
| Linear coefficient of thermal expansion | (23-80)°C | DIN 53 752 | 0.8-1.0 | K-1 |
| Heat conduction | DIN 52 612 | 0.16 | W/mK | |
| Vicat softening point | B50/oil | ISO 306:1994 | 93 | °C |
| Flame retardance | >1.4mm | UL-Standard 94 | 94HB | Class |