Properties: | Other |
---|---|
Brand Name: | Heatmed, iGloves |
Properties: | Pidegree Gloves Group |
Color: | White, black, blue, Purple |
material: | Synthenic Nitrile Latex |
Size: | Small, Medium, Large, Extra-large. |
Place of Origin: | Malaysia |
Quick Details
Specifications
-----------------------------------------------------------------------------------
1. Product Description:
Quality Standards
*Conforms to ASTM D6319 and EN 455 Standards.
*Manufactured under QSR (GMP), ISO 9001:2008 & ISO 13485:2003 (Medical Device) Quality Management System.
*Biocompatibility tested or biocompatibility friendly.
*Resists permeation by a wide range of chemicals as compared to natural rubber latex of the same thickness.
Glove sizes
*Extra-small, Small, Medium, Large, Extra-large.
*Marked in the check box on the shipping carton with black ink
-----------------------------------------------------------------------------------
2. Product Specification:
Type
* Powdered or Powder-free; non-sterile
Material
* Synthetic Nitrile Latex.
Design & Features
* Ambidextrous; Finger-textured; beaded cuff; white or coloured (blue/green/pink/light purple/black)
Storage
* the gloves shall maintain their properties when stored in a dry condition at temperature not higher than 30°C.
Shelf-life
* 5 years from the date of manufacturing.
-----------------------------------------------------------------------------------
3. Physical Dimension:
IGlove
Length(mm):
* Min.240
Width(mm)
* Extra-samll: 76 ± 3; Small: 84 ± 3; Medium: 94 ± 3; Large: 105 ± 3; Extra-large: 113 ± 3
Thinkness-single wall(mm)
* Fingers: Min. 0.05; Palm: Min. 0.05
ASTM D6319
Length(mm):
* Min. 220 (size XS,S); Min. 230 (size M, L, XL)
Width(mm)
* Extra-samll: 70 ± 10; Small: 80 ± 10; Medium: 95 ± 10; Large: 111 ± 10; Extra-large: 120 ± 10
Thinkness-single wall(mm)
* Fingers: Min. 0.05; Palm: Min. 0.05
-----------------------------------------------------------------------------------
4. Product Properties:
ASTM D6319
Elongation at break(%)
* Before Aging: Min. 500; after Aging:Min. 400
Tensile Stength(Mpa)
* Before Aging: Min 14; after Aging: Min14
Force at Break(N)
* Before Aging: N/A; after Aging: N/A