Brand Name: | DC silicone |
---|---|
Color: | white or custom |
Sample: | 1kg sample is available |
appearance: | liquid |
MOQ: | 100kgs |
Model Number: | DC-C30 |
Place of Origin: | China (Mainland) |
Hardness: | 30 Shore A |
Mixing ratio: | 2%-5% |
Curing time: | 3-5 Hours |
HS code:: | 39100000 |
Material: | 100% Silicone |
Type: | condensation cure silicone rubber |
Brand Name: | DC SILICONE |
Sample: | 1kg free sample |
Quick Details
Specifications
Application
DC-C30RTV-2 Mold MaKing Silicone Rubber is used for making molds of concrete stone, GRC(Glass-fiber Reinforced Composite), gypsum decoration, plaster ornaments, fiberglass products, polyester decoration, unsaturated resin crafts, polyresin crafts, polyurethane, bronze, wax, candle, and similar products.
Description
DC-C30RTV-2 Mold Making Silicone Rubber Is a kind of room temperature vulcanized silicone rubber in condensation type. It's Generally named asTwo Part silicone rubber, Part A is a flowable liquid Silicone,PArt B is the curing agent (Tin catalyst). It'S mainly used for mold making.
Technical Parameters
DC-C30 Silicone rubber with moderate hardness in high tensile and tear strength,which is suitable for middle or large size product with pattern by both pouring and brushing operation,especially popular for manufacturer of gypsum decoration and concrete molding,It is one of our best selling silicone.
Model |
Color |
Mixing ratio (%) |
Pot life (mins, under 25℃) |
Curing time (hrs,under 25℃) |
Hardness ( Shore A ) |
Tensile- Strength (MPa) |
Tear- Strength (kN/m) |
Viscosity (after A/B mixed,mPa.S) |
Shrinkage Rate (%) |
Elongation (%) |
DC-C30 |
White |
2 |
30-40 |
3-5 |
30±2 |
>4.2
|
>25
|
27000±5000
|
≤0.25% |
>450% |
Operation instructions
Step 1: prepare the original molds
MAke your original molds perfect. Fix it on a board. and fix the original mold on a board, then used four piece of board to enclose the original molds.
Step 2: Take 100 G parts A and add2G parts B and mix them evenly.
Notes: Mold MakingSilicon rubber is a kind of flowing liquid,it contains two parts. Part A is a kind of flowing white liquid and part B is the curing agent or catalyst.Pls follow the step strictly:
1.Weigh the two part exactly by electronic weight. If not, for example add too much catalyst, the operation time will be too fast to operate,which will cause inconvenience to operate.
2.MIx part A and part B evenly. OTherwise the silicon rubber will be partly solidified and this will give birth to difficulties in your final operation. What's more, the finished molds will meet a short life. All of these will cause a waste of silicon rubber.
Step 3: Vacuum pumping
without exception, this step takes less than 10 minutes. Otherwise, it will cause, and no more further steps will be available.
Step 4: PourIng casting or Brush operation
Notes:1. for simple pattern products we suggest use pouring operation way, which will be very easy to operate and demould. Pourable silicone require low viscosity which will be easy to flow smoothly and easy to de-air.
2.for delicate pattern products we suggest use brushing operation way, which can copy the pattern exactly. Brushable silicone require high viscosity which won'T be easy to flow away and easy to brush.
3.We sugges to set the silicone mold for another 12 hours after demould before you put it into a large production.
PAckage
25KG/Drum vacuum packing for part A +1kg/ bottle catalyst for part B;9/18drums/pallet;
200KG/Drum packing for part A +1kg/ bottle catalyst for part B; 1//2/4drums/pallet;
SHelf life
Twelve(12) months when storedunder Dry and cool place by original package under25℃
MInimum order of quantity(MOQ)
200KG